Corresponding to other steel mill grades:SLD DC11 XW-41 1.2379
Specialty:
- A maximum hardness of 62 HRC increases wear resistance by about 35%
- Adhesion of surface treatment films (CVD etc.) increased by about 30%
- The heat treatment change is reduced by about 40%, and the shape deviation will also improve
- Cutting about 35%
Purpose | Use the hardness | Purpose | Use the hardness |
blanking die | 58~62HRC | advanced gauge | 60~65HRC |
Molded roll | 58~63HRC | Rubbing wire | 60~63HRC |
The screw forming die of cross groove | 57~62HRC | the die die of transformer core | 58~62HRC |
Stretch die | 58~63HRC | cold upsetting die | 58~62HRC |
Scissors | 50~65HRC | thermosetting resin molding mold | 56~61HRC |
Chemical constituents%
C | Si | Mn | P | S | V | Cr | Mo | - | Factory Status |
1.40/1.60 | ≤0.40 | ≤0.60 | ≤0.030 | ≤0.030 | 0.60/1.10 | 11.00/13.00 | 0.70/1.20 | - | Annealing HB≤255 |
Comparison of characteristics
Steel | SLD | 8%Cr | 10%Cr | SKD11 |
Hardness (HRC) |
60~62 | 61~63 | 59~61 | 58~60 |
Wear resistance | A | B | B | A |
Surface treatment | A | C | C | B |
Toughness | B | B | C | C |
Machinability | B+ | C | B | D |
Heat treatment in inches | A | C | C | B |
Weldability | B | B | C | C |
Heat treatment
Relationship between quenching temperature, residual Austrian volume and